Founded in 2002, headquartered in Chengdu National Industrial Park- Meishan Jinxiang Industrial Park.
The largest FKM manufacturer
in China, with the actual output is 5500mt in 2022 which is the total sum of No.2 - No.5.2 CNAS approved labs;
1 10,000 clarification workshop
for smart-wearable devices;
1 100,000 clarification workshop
for FKM precompounds and compounds.13 producing lines
for FKM precompounds and compounds.Actual full capacity is 14000mt per year.

F Content
Min 66%
Specific Gravity
Min1.92
Physical form
Slab
Color
VARIOUS
Solubility
Ketones and Esters
Hardness (shore A)
75±5
Safety and handling
Store in well ventilated place
Smoking is forbidden Strictly in working areas
Avoid eye contact
Wash thoroughly any contacted skin and clothing after handling
Typical Physical Properties
Press Cure 180ºC@5min,
Post Cure 230ºC@24hour
Hardness, Shore A
75±5 (ASTM D 412)
Elongation at Break, % Min200
(ASTM D 412)
Tensile, MPa
Min11.0
(ASTM D 2240)
Compression set % 200ºC@70hour,
Max15 (ASTM D 395 method
B Disc)
Low Temperature Resistance
Brittleness temperature, ºC
-26
(ASTM D 1329)
Air oven aging
ASTM D-537, 230ºC@70h
Hardness change, degree
2
Tensile change %
-2
Elongation at break change %
0
Oil resistance ASTM D471 standard, 150ºC@70h
ASTM 1# standard oil
Tensile change %
0
Volume Change %
0.4
ASTM 3# standard oil
Hardness change, degree
6
Tensile change %
-4
Elongation at break change %
2
Volume Change %
2.1
Typical Physical PropertiesPress Cure 180ºC@5min,
Post Cure 230ºC@24hourHardness, Shore A
75±5 (ASTM D 412) Elongation at Break, % Min200
(ASTM D 412) Tensile, MPa
Min11.0
(ASTM D 2240) Compression set % 200ºC@70hour,
Max15 (ASTM D 395 method
B Disc)
Low Temperature ResistanceBrittleness temperature, ºC
-26
(ASTM D 1329)
Air oven aging
ASTM D-537, 230ºC@70h
Hardness change, degree
2
Tensile change %
-2
Elongation at break change %
0
Oil resistance ASTM D471 standard, 150ºC@70hASTM 1# standard oilHardness change, degree
2
Tensile change %
0
Elongation at break change %
0
Volume Change %
0.4
ASTM 3# standard oilHardness change, degree
6
Tensile change %
-4
Elongation at break change %
2
Volume Change %
2.1

20kgs/25kgs
per carton by courier, like FedEx, DHL etc; 500kgs/625kgs/700kgs per pallet for shipping.
Installation Instructions

ISO9001, ISO14001, IS016949
Currently has 65 patents, 15 invention patents are under application, participated in the formulation of 4 National Standards.

1, What's your MOQ?
BY air MOQ is 20-25KG, by sea MOQ is 100KG.
2, What's your delivery time?
For stock goods, we can arrange delivery within 3 working days, otherwise delivery time is around 7-14 working days.
3, What's your package?
Usually goods are
packaged with PE film in carton. The weight is 20-25kg net per carton. 500kgs/625kgs/700kgs
in a pallet.
4, How can we select the exactly grade which suit for our usage?
Please contact our sales, we'll recommend suitable grade according to your typical physical properties and other related information.