Place of Origin | Zhejiang, China |
Standard | ASTM GB DIN |
Grade | H13 |
Delivery Time | 31-45 days |
Application | Mold making |
Thickness | 20-500mm |
Tolerance | ±3% |
Processing Service | Punching, Cutting, milling |
Product Name | Alloy steel |
The length of the | 200-6000mm |
The width of the | 50-1000mm |
Surface treatment | Black leather or milled |
species | Stainless steel |
The thickness of the | 20-500mm |
technology | Electroslag, forging, vacuum degassing |
Selling Units: | Single item |
Single package size: | 13X5X3 cm |
Single gross weight: | 10.000 kg |
Product Description
Method of smelting
Medium frequency furnace +LF
Characteristics of the
(1)It has high hardenability and toughness
(2)Excellent thermal cracking resistance and can be used for water cooling in the workplace
(3)With moderate wear resistance, carburizing or nitriding process can also be used to improve the surface hardness, but slightly to reduce the resistance to hot cracking
(4)Due to low carbon content, the secondary hardening ability of tempering is poor
(5)It is resistant to softening at higher temperatures, but the hardness decreases rapidly when the temperature is higher than 540 °C (1000 °F)
(6)The deformation of heat treatment is small
(7 Medium and high machinability
(8)Medium resistance to decarbonization
List of chemical composition(%)
Medium frequency furnace +LF
Characteristics of the
(1)It has high hardenability and toughness
(2)Excellent thermal cracking resistance and can be used for water cooling in the workplace
(3)With moderate wear resistance, carburizing or nitriding process can also be used to improve the surface hardness, but slightly to reduce the resistance to hot cracking
(4)Due to low carbon content, the secondary hardening ability of tempering is poor
(5)It is resistant to softening at higher temperatures, but the hardness decreases rapidly when the temperature is higher than 540 °C (1000 °F)
(6)The deformation of heat treatment is small
(7 Medium and high machinability
(8)Medium resistance to decarbonization
List of chemical composition(%)
project
C
Si
Mn
S
P
Cr
Mo
Ni
The minimum
0.32
0.80
0.20
4.75
1.10
The biggest
0.45
1.20
0.50
0.03
0.03
5.50
1.75
0.25
C
Si
Mn
S
P
Cr
Mo
Ni
The minimum
0.32
0.80
0.20
4.75
1.10
The biggest
0.45
1.20
0.50
0.03
0.03
5.50
1.75
0.25
A) Minimum order quantity?
1 ton
B) What are your payment terms?
Wire transfer or as per your request
C) What are your working hours?
8:00 am -- 17:00 PM (Beijing Time, 08.00 GMT)
D) Your delivery date?
20days -40days, also according to material requirements
1 ton
B) What are your payment terms?
Wire transfer or as per your request
C) What are your working hours?
8:00 am -- 17:00 PM (Beijing Time, 08.00 GMT)
D) Your delivery date?
20days -40days, also according to material requirements
Good price H13 tool steel hot rolled or hot forged, 1.2344 plate/flat/block steel 19 years of industry experience
$2.5 ~ $2.7
Consumer electronics Industry Chain · Alloy steel · Other Special Steel Products